? Honesty produce value, the achievements you can only communicate with me. Look forward to your call! Contact: Liu Haiyang Tel: 18291703919 QQ: 3228413769 E-mail: bairongti@126.com Website: www.sxbrti.com Shaanxi 100 Yung Metal Product Co. Titanium Table: Industrial titanium plate: TA1, TA2, TA3, TA4, TA5 , TA6, TA7, TA8, TA8-1, TA9, TA9-1, TA10, TA11, TA15, TA17, TA18, TC1, TC2, TC3, TC4, TC4ELI, TB2, TB5, TB6, TB8 manufacturing process: hot, Cold rolled specification (thickness * width * length (mm)): Hot-rolled: (4.0 -12) * (600-1050) * (1000-2500) cold-rolled: (0.5 to 4.0) * (600-1050) * ( 1000-2500) Delivery state: R, M, Y, ST implementation of standards: GB / T3621-2007 GJB, ASTM, AMS, AMSE, MIL, JIS basic properties of TC4 titanium alloy TC4 introduce heat treatment:? TC4 material solute After hardening, the strength increase is not, also to 1100MPa, the strength of the annealed condition is generally 900MPa? TC4 coefficient of thermal expansion? TC4 titanium alloy with excellent corrosion resistance, low density, high specific strength and good toughness and weldability and a series of advantages in aerospace, petrochemical, shipbuilding, automotive, pharmaceutical and other sectors have been successfully applied. ? TC4 titanium alloy mechanical properties:? Tensile strength σb (MPa) ≥895, provides residual elongation stress σr0.2 (MPa) ≥825, elongation δ5 (%) ≥10, section shrinkage ψ (%) ≥ 25 TC4 titanium density:?? 4.5 (g / cm3) Operating temperature -100 ~ 550 (℃) TC4 titanium alloy chemical composition:? TC4 titanium (Ti) margin, iron (Fe) ≤0.30, carbon (C) ≤0.10, nitrogen (N) ≤0.05, hydrogen (H) ≤0.015, oxygen (O) ≤0.20, aluminum (Al) 5.5 ~ 6.8, vanadium (V) 3.5 ~ 4.5 titanium sheet manufacturing process described in the metal and then forging above the crystallization temperature of forging processes. Rolling the hot rolling process at a temperature above the recrystallization temperature. Cold-plastic deformation temperature is lower than the temperature of the rolling process reply. Annealing: The metal was slowly heated to a certain temperature, maintaining sufficient time, then a suitable rate of cooling (usually slow cooling, sometimes controlled cooling) a metal heat treatment process. Pickling: The article is immersed in an aqueous solution of sulfuric acid or the like, to remove the oxide film such as a metal surface. Before treatment or intermediate processing plating, enamel, rolling and other processes. Application density titanium titanium and titanium alloy is small, high tensile strength, in the range of -253-600 ° C, his strength is almost the highest in the metallic material, it can be formed thin in an appropriate oxidizing environment and hard oxide film, having excellent corrosion resistance. In addition, it has a non-magnetic, low coefficient of linear thermal expansion characteristics. This makes titanium and alloy called first major aerospace structural materials, and subsequently extended to ship manufacturing, chemical industry and other fields, and has been developing rapidly. Especially in the chemical industry, more and more products are used in titanium and titanium alloy products, such as petrochemicals, fiber, paper pulp, fertilizer, electrochemical desalination and other industries, in exchange, a reaction tower, synthesizer, autoclave and so on. Wherein titanium is used as the electrolytic plates, the electrolytic cell and water desalination in a reaction column, the reaction vessel is used as the tower and the kettle body and the like. ? With the development of science and technology, the applications of titanium are increasingly broad, such as medical, automotive, sports, etc., these are real reaction out of titanium as a light metal, it has the good characteristics more and more perceived by people and can be, and is the fastest replaced by other metals into our production applications, and even our bodies were. Titanium work in humid atmosphere and seawater, which is far superior corrosion resistance of stainless steel; for pitting, etching, stress corrosion resistance is particularly strong; alkali, chloride, chlorine, organic materials, nitric acid, sulfuric acid etc. have excellent corrosion resistance. However, the corrosion resistance of titanium with a reduction of oxygen and chromium salts medium is poor. ??